Mechanical and Electromagnetic Properties of Carbon Fiber Toughened Si3N4 Ceramic Composites

Qinggang Li, Yuhang Du, Ning Sun, Jinkai Li, Mengyong Sun, Guopu Shi

Carbon fiber-reinforced Si3N4 ceramic materials were prepared by hot pressing sintering process using silicon nitride as substrate and short carbon fiber reinforcement. The mechanical properties, microstructure and electromagnetic properties of the sintered samples were evaluated. Experimental results show that atmosphere hot pressing can reduce the sintering temperature of Si3N4 ceramics and promote phase transition. When the additional amount of carbon fiber is 3.0 wt%, the sintering temperature is 1700°C, the holding time is 30 min, forming pressure is 30 MPa, the sintered sample has the best extensive properties: hardness (>8.5 GPa) and density (>2.8 g/cm3) meet the engineering needs, fracture toughness is enhanced by 22.7%, fracture toughness can reach 8.11 MPa•m1/2, dielectric properties are also improved.

索引于

哥白尼索引
打开 J 门
学术钥匙
研究圣经
引用因子
宇宙IF
参考搜索
哈姆达大学
学者指导
国际创新期刊影响因子(IIJIF)
国际组织研究所 (I2OR)
宇宙
日内瓦医学教育与研究基金会
秘密搜索引擎实验室

查看更多